LED UV833 series of UV curing offset printing ink is suit for LED UV dry ways.Suit for fast printing.
Model name :
LED UV833 Offset Ink ManufactureOrder Quantity(MOQ) :
1KGPayment :
T/T Or L/CProduct Origin :
Made in ChinaColor :
Magenta/Yellow/Cyan/Black/WhiteShipping Port :
Fuzhou of ChinaLead Time :
According to order quantity.If order more than 10 tons it should be take 35 days to producePackage Weight :
CMYK Color 1KG per tin,White color ink 1.5 kgs per tin1.Introduction
This product is mainly composed of LED UV curable acrylic acid resin, photoinitiator,active diluent, pigment filler and various additives.It is an environment-friendly ink product with no solvent and volatile raw material ingredients, balanced by professional technical formula, with stable printing suitability, fast curing speed,bright ink color, high saturation, good adhesion, excellent aging resistance and other advantages.
Suitable for 385 and 395 wavelengths,LED UV Lamp power not less than 8kw
Applicable substrates include: aluminum plated gold and silver card paper,
laser card paper, surface treated PVC, PET.
LED 833 | YELLOW | MAGENTA | CYAN | BLACK | |
DM | 33 - 36 | 34 - 37 | 34 - 37 | 34 - 37 | |
Tack | 11.0-13.0 | 12.0-14.0 | 12.0-14.0 | 12.0-14.0 | |
Drying method LED | >80mj/cm2 | >80mj/cm2 | >80mj/cm2 | >80mj/cm2 | |
PARTICLE SIZE | Below 10㎛ | Below 10㎛ | Below 10㎛ | Below 10㎛ | |
Adhesion | Coated paper (paper) | Excel | Excel | Excel | Excel |
Gold and silver card | Excel | Excel | Excel | Excel | |
RUB REISTANT | 4.0(5Excel - 1Poor) | 4.0(5Excel - 1Poor) | 4.0(5Excel - 1Poor) | 4.0.(5Excel - 1Poor) |
LED 833 | YELLOW | MAGENTA | CYAN | BLACK |
Acid 5(excel)-1(poor) | 5 | 2 | 5 | 5 |
Alkaline 5(excel)-1(poor) | 5 | 2 | 5 | 5 |
Water 5(excel)-1(poor) | 5 | 4 | 5 | 5 |
Alcohol 5(excel)-1(poor) | 4 | 4 | 5 | 5 |
Lightfastness 8(excel)-1(poor) | 4 | 4 | 8 | 8 |